Product Description of Rongsheng Best Price Refractory Fireclay
High Performance Low Porosity Fireclay Bricks For Glass Kiln
Fire clay bricks contain 30-50% Al2O3. During production, clay
chamotte is first mixed with refractory clay powder, then combined
with clay aggregate to form a dry mud, which is then shaped under
high pressure and sintered at approximately 1400°C. At high
temperatures, fire clay bricks exhibit weak acidity and have
limited resistance to alkaline slag erosion. However, as the Al2O3
content increases, their thermal stability surpasses that of silica
bricks and magnesia bricks.
Product Features of Rongsheng Best Price High Performance Low
Porosity Fireclay Bricks For Glass Kiln
Low porosity fireclay bricks offer several key features that make
them ideal for glass kilns:
1. Low Porosity:
This is the defining characteristic. With minimal voids or holes,
they resist penetration by molten glass and other corrosive
materials. This extends the lifespan of the kiln lining and reduces
the risk of glass contamination.
2. High Refractoriness:
They can withstand extremely high temperatures (around 1400-1600°C)
without melting or deforming. This is crucial as glass kilns
operate at very high temperatures for melting the glass.
3. Strong Resistance to Wear and Erosion:
The dense structure minimizes wear and tear from molten glass flow
and harsh chemical environments within the kiln. This translates to
better durability and longer service life for the kiln lining.
4. Good Thermal Shock Resistance:
They can withstand rapid temperature changes without cracking or
spalling. This is important for maintaining consistent temperatures
within the kiln and preventing structural damage.
5. Good Thermal Conductivity:
They efficiently conduct heat, ensuring even heat distribution
throughout the glass melt. This contributes to efficient glass
melting and minimizes temperature variations within the kiln.
6. High Mechanical Strength:
The dense structure provides good mechanical strength, allowing the
bricks to handle the weight of the glass and other materials within
the kiln without collapsing.
7. Good Chemical Resistance:
They resist chemical attack from molten glass and other chemicals
present in the kiln environment. This prevents degradation and
maintains the integrity of the kiln lining.
In summary, low porosity fireclay bricks offer a combination of
high-temperature resistance, wear resistance, thermal stability,
good heat transfer, and strong structure, making them a reliable
and long-lasting choice for glass kiln applications.
Product Application of Low Porosity Fireclay Bricks For Glass Kiln:
1) Cement and other building materials industry kiln back
insulation;
2) Petrochemical, metallurgical, ceramics, glass industry, the
furnace lining insulation;
3)Heat treatment furnace backlash insulation;
4)Non-ferrous metal industry back insulation;
5)High temperature reaction, heating equipment back insulation
insulation
Product Parameters of Low Porosity Fireclay Bricks For Glass Kiln
| Item | Indicator |
|---|
| DN-11 | DN-14 | DN-17 |
| Chemical Composition | Al2O3 / %
| μ ≥ | 47 | 45 | 42 |
| σ ≤ | 1.0 | 1.0 | 1.0 |
| Fe2O3 / % | μ ≤ | 1.2 | 1.5 | 1.8 |
| σ ≤ | 0.2 | 0.2 | 0.2 |
| Physical Properties | Bulk Density / (g/cm³)
| μ ≥ | 2.40 | 2.34 | 2.26 |
| σ ≤ | 0.02 | 0.02 | 0.02 |
Apparent Porosity / %
| μ ≤ | 11 | 14 | 17 |
| σ ≤ | 1.0 | 1.0 | 1.0 |
Compressive Strength / MPa
| μ ≥ | 80 | 55 | 50 |
| σ ≥ | 10 | 10 | 10 |
| x_min | 70 | 55 | 40 |
| Refractoriness Under Load T0.6 / ℃ | μ ≥ | 1520 | 1470 | 1430 |
| σ ≤ | 10 | 10 | 10 |
Permanent Linear Change 1400℃×2h
| L-U | - | +0.1-0.2 |
| σ | - | 0.02 |
Permanent Linear Change 1500℃×2h
| L-U | +0.1-0.2 | - |
| σ | 0.02 |